N ° de Modelo: various Tile Tile Shape: Roll Espessura: 3.0mm Tratamento de Superfície: Roll Coated Certificação: ISO Uso: Concrete Joint Certificado: ISO9000 Szie: Padrão ou Personalizado Especificação: As Drawing Requirements Código HS: 522338 Tipo: Building Sealing Material Material: HDPE Tipo de telha de teto: Borracha Função: Impermeável Cor: Preto, Vermelho Mercados de exportação: Taxa de expansão global: mais de 350% Marca: JianFeng Origem: Hebei, China Informações de contato \ nGerenciador de vendas: kent \ nTelefone móvel: + 86-15233296877 \ nTel : 86-318-5106277 \ nFax: 86-0318-5106277 \ nWebsite: www.prolianz.com \ nEmpresa: Hengshui Jianfeng Engineering Rubber co., LTD. \ n \ n \ n \ n
Description Expansion under the influence of water with the water of water stop expansion properties of water putty and meet water swelling rubber strip. Encounter water swelling rubber is a new special kind of rubber products. It is a combination of general rubber products performance, and can meet the expansion of the water on its own performance, is a new type of waterproof material, water stop, waterproof effect is more reliable than ordinary rubber. Putty type of expansive water stop under the influence of water is a recently developed new products, it has met the special performance for the expansion of the water. Elasticity of the material in water sealing waterproof effect, when both sides joint lateral distance to elastic recovery rate of elastic waterproof material, due to the nature of the material has the water expansion. Starting and ending water in material expansion scope can still function. |
Advantages 1,This product can be put on the base surface of concrete construction joint directly, and the construction is convenient, simple. 2,In a few minutes after this product in water gradually expand, on the one hand, blocking all ooze water gap, on the other hand combined tightly with concrete interface, and fundamentally to cut off the water seepage channel. 3, the main body material is inorganic mineral material, so it have ageing resistance, corrosion resistance, permeability resistance function and is will not affected by temperature and humidity changes, has reliable durability. 4, Have remarkable self-healing function, when the construction joints emergent a new tiny crack, it can continue to swell, water stop further blocking new micro seam, automatic reinforcement waterproof performance. 5, In the process of cement mortar pouring, the bibulous rate is very small ,it will not because of the existence of the mixing water and caused concrete expansion . 6, This product after repeated ,no main material leachingimmersion material leaching, no shivers And the performance of expansion under the influence of water to maintain is good. |
Application method 1,cast-in-site concrete construction joint, will have the construction of concrete base, chisel, the strip of water stop paper take out, in the central along the longitudinal width of construction joint, and to give pressure together, every 50 cm interface built with adhesive glue overlap and compaction, up and down with masonry nail nails. 2, concrete cracks, the crack width of each 4 cm slot, will be embedded within the seam of water stop, compaction in polymer cement paint twice. |
Notes 1,Paste the interface should be kept dry. Applied to the water stop gap inside may not appear. 2, And construction joint interface of water stop paste to close, stretch along the construction joint direction shall not be broken, can't be scum dust cover, etc. 3, To fully be concrete water stop parcel, parcel thickness > 5 cm. 4, After fixation of water stop before pouring the concrete, should avoid to be soaked in water for rain or construction. 5, Storage and transport of water stop, avoid damp and extrusion, should not be stacked more than |
Items | index | |||||
B | S | J | ||||
1. Hardness ( Shore A ) | 60±5 | 60±5 | 60±5 | |||
2.Tensile strength ,MPa ≥ | 15 | 12 | 10 | |||
3.Elongation at break , % ≥ | 380 | 380 | 300 | |||
4.Compression set % | 70ºC×24h,% ≤ | 35 | 35 | 35 | ||
23ºC×168h,% ≤ | 20 | 20 | 20 | |||
5.Tear strength,KN/m ≥ | 30 | 25 | 25 | |||
6.Brittleness temperature,°C ≤ | -45 | -40 | -40 | |||
7.Air aging | 70ºC× 168h | Hardness ( Shore A ) ≤ | 8 | 8 | -- | |
Tensile strength,MPa ≥ | 12 | 10 | ||||
Elongation at break , % ≥ | 300 | 300 | ||||
100ºC× 168h | Hardness ( Shore A ) ≤ | -- | -- | 8 | ||
Tensile strength, MPa ≥ | 9 | |||||
Elongation at break , % ≥ | 250 | |||||
8. Resistance ozone ageing 50pphm: 20%, 48h | 2 grade | 2 grade | 0 grade | |||
9. Adhesion of rubber to metal | With contact section in elastomer |
Grupo de Produto : Série de parada de água > Barra de waterstop inchaço
outros produtos
produtos quentes
Aletas impermeáveis da lama das partes do corpo do caminhão semiRolamentos de panela PTFE com boa qualidade para o EquadorRolamentos de borracha de alta amortecimento com alta qualidade para os EUAVenda quente chumbo isolamento borracha rolamento para a TurquiaProtetor espiral de plástico para mangueira hidráulicaProdutos de Silicone Flexível Extrudados Mangueira de SiliconeMelhor Preço Hidrofílico Água Parar Com Vários Tamanho (made in China)Alto desempenho PVC Waterstop para concreto Joint (made in China)Tiras resistentes ao calor da borracha de silicone da porta do fornoRolamento de Borracha Esférica Padrão ASTM para a FrançaAlmofada de rolamento de borracha para construção de ponte projetando para FilipinasWaterstop de borracha quente da venda para a engenharia material impermeável da construçãoTira de borracha de EPDM para portas de carrosTira de vedação de porta de borracha autoadesiva de alta qualidadeTira refrigerada composta do selo de porta do recipiente do caminhão da personalização / perfil do PVC da portaTira de vedação de borracha de isolamento bom som de borda de janela flexível